Piezoelectric and structural properties of c-axis textured aluminium scandium nitride thin films up to high scandium content

Simple item page
dc.contributor.authorMertin, S.
dc.contributor.authorHeinz, B.
dc.contributor.authorRattunde, O.
dc.contributor.authorChristmann, G.
dc.contributor.authorDubois, M. A.
dc.contributor.authorNicolay, S.
dc.contributor.authoret al.
dc.date.accessioned2021-12-09T14:00:43Z
dc.date.available2021-12-09T14:00:43Z
dc.date.issued2018
dc.description.abstractPartial substitution of aluminium by scandium in the wurtzite structure of aluminium nitride (AIN) leads to a large increase of the piezc electric response by more than a factor of 2. Therefore, aluminium scandium nitride (ASN) thin films attracted much attention to improve piezoelectric MEMS devices such as RF filters, sensors, micro actuators and energy harvesting devices. In this work, process-microstructure-property relationships of ASN thin films containing up to 42% Sc were investigated. Like AIN thin films, ASN films are sputter deposited at 300-350 degrees C with pulsed DC powered magnetrons. The influence of the process parameters on the film structure, the intrinsic stress and the piezoelectric response was investigated in order to achieve optimal piezoelectric coefficients up to high Sc concentrations. X-Ray diffraction (XRD) and transmission electron microscopy (TEM) were used to analyse the quality of c-axis texture. The films showed exclusively (002) texture with rocking-curve widths in the range of 1.3-2 degrees (FHWM). The films were further analysed by scanning electron microscopy (SEM). The Sc content was determined by energy-dispersive X-ray spectroscopy (EDX). A good compositional homogeneity in the range of 0.5-1 at% was achieved between border and centre of 200-mm wafers. So far, we obtained ASN films with transversal piezoelectric coefficients of up to e(31,f) = 2.77 C/m(2), which is a factor 2.6 higher than in pure AIN thin films.
dc.identifier.citationSurface and Coatings Technology, vol. 343, pp. 2-6, Jun 2018.
dc.identifier.doihttps://doi.org/10.1016/j.surfcoat.2018.01.046
dc.identifier.urihttps://hdl.handle.net/20.500.12839/238
dc.subjectAluminium scandium nitride, Piezoelectric thin films, Reactive magnetron, sputtering, C-axis texture, Electron microscopy, X-ray diffraction, bulk acoustic resonators, Materials Science, Physics
dc.titlePiezoelectric and structural properties of c-axis textured aluminium scandium nitride thin films up to high scandium content